The PU010 adhesiveis ideal for quick installation of insulation and acoustic panels, SATE and roof insulation. Suitable for use on many different substrates including masonry, concrete, wood and metal.
PU010.
CARACTERISTICS
.
- An easy-to-use alternative to drywall mortars and adhesives
- All-purpose, easy-to-use alternative to drywall mortars and adhesives.
- Ideal for bonding drywall, insulation and SATE
- Ideal for bonding drywall, insulation and SATE.
- Forms a high-strength bond after only 40 minutes
- Expands to fill voids, cavities, and uneven surfaces
- Compatible with a wide range of substrates in construction
- Charging time after approximately 3 hours
- Fast curing, skin formation in 10 minutes
- No subsequent expansion or contraction
SPECIFICATIONS
.
Features . |
Standard Norm |
Classification |
Classification |
. | ||||
Reaction to fire |
DIN 4102-1 DIN 4102-1 |
B2/B1 B2/B1 |
||||||
Type of foam |
NBS |
|||||||
Quality |
EIFS |
|||||||
Component system |
Component monocomponent |
|||||||
Propellents |
Yes |
|||||||
Aerosol temperature limit |
10 ºC - 30 ºC |
|||||||
Ideal aerosol temperature |
20 ºC |
|||||||
Ambient limit temperature |
5 ºC - 35ºC* |
|||||||
Density |
LAB 015 LAB 015 |
15 - 25 |
||||||
Skin formation (min) |
FEICA TM 1014 |
10 |
||||||
Cutting time (min) |
FEICA TM 1005 |
35 |
||||||
Capacity of load (hour) |
3 |
|||||||
Performance |
FEICA TM 1003 |
30 l |
||||||
Thermal conductivity (mW/m.K) |
EN 12667 |
36 |
||||||
Elasticity at break (%) / dry |
FEICA TM 1018 |
14 |
||||||
Compressive strength @ 10% (kPa) / dry |
FEICA TM 1011 |
44 |
||||||
Compressive strength @ 10% (kPa) / wet |
32 |
|||||||
Shear strength (kPa)/dry |
FEICA TM 1012 |
51 |
||||||
Temperature resistance (long term) (°C) |
-40 ºC - 90 ºC |
|||||||
Temperature resistance (short term) (°C) |
-40 ºC - 130 ºC |
. | ||||||
COV (%) |
17.49 |
|||||||
COV (g/l) |
180.00 180,00 |
|||||||
Conservation |
24 months |
APPLICATION TIPS
.
- Shake the bottle vigorously at least 20 times.
- Remove the protective cap from the canister and place the top end on the illbruck PU foam gun adapter.
- Remove the protective cap from the canister and place the top end on the illbruck PU foam gun adapter.
- Spray a bead of illbruck PU010 adhesive foam around the perimeter and in the center of the back of the insulation material.
- Always handle the canister in an upright position for best results and make sure the valve is facing downward.
- Move the panel into place and press firmly to ensure good contact. Hold in position for 2-3 minutes. Heavy panels may require additional support during curing.